Epoxy Glass
Glass plates – Epoxy
HGW 2372 Y 2372.4 standard 7735
Plates epoxy fiberglass laminate is manufactured using glass cloth impregnated with epoxy resins. Excellent electrical and mechanical behavior. High dimensional stability.
FEATURES | UNIT | VALUE | |
TYPE AS STANDARD DIN 7735 | Hgw 2372 | Hgw 2372.4 | |
BENDING TENSION TO BREAK PERPENDICULAR TO THE ROLLING (at 20 ºC) | Mpa | 340 | 240 |
APPARENT ELASTIC MODULUS IN BENDING | Mpa | 24×103 | 24×103 |
TENSILE STRENGTH | Mpa | 300 | 300 |
RESISTANCE TO COMPRESSION PERPENDICULAR TO THE LAYERS | Mpa | 300 | 350 |
RESISTANCE TO SPLIT PARALLEL TO THE LAYERS | Mpa | 30 | 30 |
DENSITY | g/cm3 | 1,7-2,0 | 1,7-2,0 |
TEMPERATURE INDEX | °C | 130 | 155 |
WATER ABSORPTION (for thickness 3 m/m) | mg | 8 | 13 |
Plate thickness: from 0,2 m/m to 70 m/m.
Plate formats:
1000×1000 m/m.
2000×1000 m/m.